Austenitic

is not hardenable through heat treatment

Ferritic

is not hardenable through heat treatment

Martensitic

is hardenable through heat treatment

Precipitation Hardening

is hardenable through low temperature heat treating
when properly "conditioned or "solution" treated before aging